This alloying element-saving hot rolled duplex stainless steel material contains, by mass %, C: 0.03% or less, Si: 0.05% to 1.0%, Mn: 0.5% to 7.0%, P: 0.05% or less, S: 0.010% or less, Ni: 0.1% to 5.0%, Cr: 18.0% to 25.0%, N: 0.05% to 0.30% and Al: 0.001% to 0.05%, with a remainder being Fe and inevitable impurities, wherein the alloying element-saving hot rolled duplex stainless steel material is produced by hot rolling, a chromium nitride precipitation temperature TN is in a range of 960° C. or lower, a yield strength is 50 MPa or more higher than that of a hot rolled steel material which is subjected to a solution heat treatment, and the alloying element-saving hot rolled duplex stainless steel material is as hot rolled state, and is not subjected to a solution heat treatment. This clad steel plate includes a duplex stainless steel as a cladding material, the duplex stainless steel has the above composition, and the chromium nitride precipitation temperature TN is in a range of 800° C. to 970° C.