Provided is a rubber composition, which is excellent in fuel permeation resistance, and is capable of achieving improvements in low-temperature embrittlement property and solvent crack property. The rubber composition includes: a fluororubber having a fluorine concentration content of 70 to 71 wt % as a main component; a crosslink-type agent; and the following components (A) and (B), in which: the total content [(A)+(B)] of the above-mentioned components (A) and (B) falls within the range of 17 to 25 parts by weight with respect to 100 parts by weight of the above-mentioned fluororubber; and a weight ratio (A)/(B) of the content of the above-mentioned component (A) to the content of the above-mentioned component (B) falls within the range of 2.0/1 to 3.0/1: (A) barium sulfate; and (B) a neutral silica.