A conventional composition of carbon nitride has a deposition method and properties limited. In the case of using the composition of carbon nitride as a protective film, for example, a material of an object to be coated (goods) is required to satisfy with a condition in disagreement with a temperature during forming the composition of carbon nitride. Besides, in the case of using the composition of carbon nitride as an insulating film in a semiconductor device, low stress relaxation and low coverage for a step are produced since the insulating film has a low hydrogen concentration. Consequently, a composition including carbon nitride according to the present invention is formed at a deposition temperature that enables to include hydrogen in the composition at 30 to 45 atomic %, for example, at temperatures of 100° C. or less, preferably 50° C. or less, more preferably from 20° C. to 30° C., with stability and adhesiveness kept.