A method for forming hollow silica spheres by dissolving a hydrolyzable aryl silane in an aqueous solution of water and an acid to form a hydrolyzed silane solution, mixing the hydrolyzed silane solution with a hydroxide base to form a precipitate, and calcining the precipitate in a multi-stage calcination procedure that includes (a) heating to a first temperature of 180 to 240° C. with a first ramp rate of 3 to 10° C./min and holding the first temperature for 2 minutes to 2 hours, then (b) heating to a second temperature of 600 to 740° C. at a second ramp rate of 0.1 to 4° C./min, and holding the second temperature for 2 to 24 hours.