The present invention provides a Nd—Fe—B magnet including a first film of aluminum having a first predetermined hardness and an anti-corrosive coating of oxidized aluminum having a second predetermined hardness on the first film. The second predetermined hardness is at least eight times the first predetermined hardness. The present invention also provides a method for preparing a hard aluminum film on the Nd—Fe—B magnet. The method includes depositing the first film on the Nd—Fe—B magnet under vacuum, disposing the Nd—Fe—B magnet having the first film on the anode, and subjecting the Nd—Fe—B magnet having the first film to the anodic oxidation process under a solution containing an electrolyte present between 15 wt. % to 20 wt. % to form the anti-corrosive coating on the first film to prevent the Nd—Fe—B magnet from corroding. The electrolyte is selected from at least one of sulfuric acid, chromic acid, boric acid, and oxalic acid.